Strengthening of face impulse seals rings by electroerosive alloying method

Abstract

The results of the metallographic and durametric studies of the samples made of steel 40X (40H), 12X18H10T (12H18N10T) and 38Х2МЮА (38H2MUA) steel grades; nickel alloy ХН58МБЮД (HN58MBUD) and beryllium bronze БрБ2 (BrB2) with combined electroerosive coatings are presented. It has been found that the most preferable coatings for the steel substrates are the strengthening coatings having the composition of BK8 + Cu + BK8 (WC8+Cu+WC8), and those for the nickel alloy of ХН58МБЮД (HN58MBUD) are the ones having the compositions of BK8 + BK8 + Cu (WC8+ WC8+Cu) and BK8 + BK8 + Ni (WC8+WC8+Ni) that are formed on the surfaces previously cemented by the electroerosive alloying method (CEEA). To strengthen beryllium bronze, there is recommended the method of electroerosive alloying (EEA) by a chromium electrode with preliminary and final CEEA.

Упрочнение колец импульсных терцевых уплотниений методом электроэрозионного легирования 34 Представлены результаты металлографических и дюрометрических исследований образцов, изготовленных из сталей 40Х, 12Х18Н10Т и 38Х2МЮА, никелевого сплава ХН58МБЮД и бериллиевой бронзы БрБ2 с комбинированными электроэрозионными покрытиями (КЭП). Установлено, что для стальных подложек наиболее предпочтительным является покрытие состава ВК8 + Cu + ВК8, а никелевого сплава ХН58МБЮД, составов ВК8 + ВК8 + Сuи ВК8 + ВК8 + Ni, сформированные на предварительно цементируемых методом электроэрозионного легирования (ЦЭЭЛ) поверхностях. Для упрочнения бериллиевой бронзы рекомендуется электроэрозионное легирование (ЭЭЛ) хромовым электродом с предварительной и окончательной ЦЭЭЛ.